公司名称：山东先达资源发展有限公司

ER316 符合：YB/T5092 2H08Cr19Ni12Mo2Si
不锈钢焊丝 相当：AWS A5.9 ER316
ISO 14343-B-SS316
In accordance with：YB/T5902 2H08Cr19Ni12Mo2Si
Be equivalent to：AWS A5.9ER316
ISO 14343-B-SS316


说明： ER316 焊丝主要成分是18Cr-12Ni-2Mo。配用SJ601不锈钢碱性烧结焊剂，其焊缝金属具有良好的力学性能和抗晶间腐蚀性能，焊缝抗裂性良好；具有不增C，且Cr、Ni烧损小等特点。因合金含量高，耐腐蚀性能优良。
用途： 长应用于石油化工、化肥、尿素生产或储存设备，如06Cr17Ni12Mo2（SUS316）等材料的焊接。
Instructions: The ER 316 welding stick consists mainly of 18Cr-12Ni-2Mo.It coordinates with the stainless steel alkaline sintered flux SJ601 .It’s welding line metal has good mechanical properties and resistance ability to intergranular corrosion and crack. It would not increase Si or C and would burn little Cr and Ni. Due to a low content of carbon, it has excellent inoxidability.
Use: It’s usually used to weld materials in petrochemical industry and production and storge facilities of fertilizer or urea, such as 06Cr17Ni12Mo2 (SUS316)

焊丝化学成分（%）
项目 C Mn Si Cr Ni Mo P S Cu
保证值 ≤0.08 1.00~2.50 0.30~0.65 18.00~20.00 11.00~14.00 2.00~3.00 ≤0.030 ≤0.030 ≤0.75
例值 0.048 1.75 0.45 19.63 12.52 2.50 0.011 0.010 0.26

焊丝直径（mm） Φ0.8 Φ1.0 Φ1.2 Φ1.6 Φ2.0 Φ2.5 Φ3.2
焊接电流（A） 70~150 100~200 140~220 50~100 100~200 200~300 300~400

注意事项：
保护气体：注意保护气体的纯度，混合气配比推荐Ar+1~3%O2。TIG采用纯Ar。
气体流量：20~25L/min。
干伸长度：15~25mm。
将焊接部位的锈层、湿气、油污、灰尘等确实除净。
室外焊接时，当风速大于1.5m/s应采取适当的防风措施，以防发生气孔。
以上建议仅供参考，在具体造作中以现场情况为准。必要时先进行工艺评定再确定焊接方案。